HMS319A/53B

Products:

Easy-to-low viscosity

Dimensional stability

Heat resistance, better alkali cement

Appropriate working hours

Better defoaming property

Uses:

1. For large mold, the mold

2.RC, GRC series of cultural stone, brick, plastic version, slate, and other replication

Operation:

1. Will be the main agent of about 1 to 2 minutes stirring, and then hardening agent into the mix 1 to 2 minutes, the speed of about 100 ~ 200rpm, do not high-speed stirring.

2. Into the vacuum devices vacuum of about 1 to 2 minutes, the exhaust about 2 times.

3. Out into the mold (the mold to be coated with release agent to facilitate demolding) natural flow levels, dry stripping.

4. Hardener recommended below 20 ℃ with 2.5%, 25 ℃ with 2.0%, 30 ℃ or above 1.5%

Hardening can be adjusted according to demand dose

Specifications:

Hardness: 20-22 ° A

Operating time: 30 ~ 40min

Touch Time: 3 ~ 4hr

Stripping time: 5 ~ 6hr

Tensile Strength: 40 +2 kgf / cm ^ 40-2 kgf / cm ^

Elongation: 450-100% 450 +100%

Tear Strength: 20 +2 kgf / cm 20-2kgf / cm

Shrinkage rate: 0.15%

Main agent: HMS319A
Color: Light gray White
Viscosity K (flow coefficient): 36,000 CPS

Hardener: HMS53B
Color: clear yellow
Viscosity K (flow coefficient): 5 ~ 10 CPS

Mixing ratio of 1.5 to 2.5