THE206A/B

Introduction:

Then can be used for industrial, impregnation coating. Handicraft transparent perfusion

Specifications:

1.78°D

2. Low viscosity, good operational

3. Transparent

4. Sclerosis shorter

USE:

1. For moisture-proof electrical and electronic components, insulation, winding package perfusion

2. Handicraft transparent perfusion

3. Handicraft then impregnated coating

4. Industrial mold infusion

Specifications:

Hardness 78 ° D

operating time: 30 minutes (measured in 100g)

Complete hardening takes about 2-4 hours

Tensile strength: 280kgf / cm ^

Anti-bending strength: 600kgf / cm ^

Compressive strength: 860kgf / cm ^

shrinkage: less 0.1%

how to use：

1. The main agent and curing agent weight ratio of 2:1 that good mixing about 2 to 3 minutes.

2. Into the vacuum devices vacuum 1 to 2 minutes, the exhaust about 2 times.

3. Remove the brush, dipping, pour, roll can be.

Note: The ratio of the amount of more, shorter operating time, easy to produce fast

Rate hardening, the deployment should be mixed according to the amount of operating conditions.